Publication
Desenvolvimento de um filme de PVC/pu resistente ao manchamento pela ganga
| datacite.subject.fos | Optimização Energética na Indústria Química | pt_PT |
| dc.contributor.advisor | Ribeiro, António Alfredo Crispim | |
| dc.contributor.author | Castro, Tatiana Glória Nunes | |
| dc.date.accessioned | 2018-03-26T10:47:51Z | |
| dc.date.available | 2019-11-15T01:30:32Z | |
| dc.date.issued | 2016 | |
| dc.description.abstract | Este trabalho foi realizado no âmbito da Tese de Mestrado em Engenharia Química – Ramo Otimização Energética na Indústria Química em parceria com a empresa Monteiro Ribas – Revestimentos. O trabalho teve como objetivo o desenvolvimento de um filme de PVC/PU que fosse resistente ao manchamento pela ganga. Para atingir o objetivo deste trabalho foram realizados ensaios que consistiram na aplicação de uma laca (aquosa ou de base solvente) em artigo de PVC ou de PU. Posteriormente à aplicação procedeu-se ao teste de resistência ao manchamento pela ganga através dos seguintes passos: manchamento do artigo com a ganga, posterior limpeza de metade da mancha, avaliação da mancha recorrendo à escala de cinzentos intervalada de 1 a 5 correspondendo o 1 à completa alteração de cor e 5 à não alteração de cor. Foram testadas lacas ou aditivos provenientes de vários fornecedores como a Rowa, a Aquitex, a Wacker, a Rudolf, a Langro e a Stahl. Foram realizados um grande número de ensaios com as lacas e aditivos fornecidos, desde lacas de base fluorpolímero, acrílica, poliuretânica, siliconada, fluorcarbono, tendo-se concluído que a utilização de uma laca de base aquosa (LW006) aditivada com ambos os produtos da Langro de base siliconada (Defender DT e defender DS) são a situação mais adequada para artigos de PU tendo conduzido aos melhores resultados. No que respeita aos artigos de PVC, as lacas da Rowa de base fluoropolímero (Rowaflon G71004, versão brilhante, e a Rowaflon M74782, versão mate) conduziram aos melhores resultados. | pt_PT |
| dc.description.abstract | This work was developed in the scope of the Master's degree in Chemical Engineering – Energy Optimization in Chemical Industry in partnership with the company Monteiro Ribas – Revestimentos. The work had as aim to develop a coating of PVC/PU resistant to denim staining. To achieve the objective of this work were done tests that consisted of applying a lacquer (water or solvent based) in a coating of PVC or PU. After the application it was performed the staining resistance test by the following steps: staining the coating with the denim clothing, cleaning half of the stain, evaluating the stain using the gray scale with measure of 1 to 5 corresponding 1 to the complete color change and 5 to no color change. Lacquers or additives were tested from various suppliers like Rowa, Aquitex, Wacker, Rudolf, Langro and Stahl. It was performed a number of tests with lacquers and additives from the suppliers from fluoropolymer, acrylic, polyurethane, silicone, fluorocarbon based lacquers and it was concluded that the use of a water-based lacquer (LW006) additivated with both products from Langro, silicone based, (Defender DT and Defender DS) was the most suitable lacquer for PU coatings due to the better results. Concerning to PVC coatings, lacquers from Rowa, fluoropolymer based, (Rowaflon G71004, bright version, and Rowaflon M74782, matte release) led to the best results. | pt_PT |
| dc.identifier.tid | 201750910 | pt_PT |
| dc.identifier.uri | http://hdl.handle.net/10400.22/11243 | |
| dc.language.iso | por | pt_PT |
| dc.subject | Lacas à base de solvente | pt_PT |
| dc.subject | Lacas aquosas | pt_PT |
| dc.subject | Rotogravura | pt_PT |
| dc.subject | Manchamento | pt_PT |
| dc.subject | Ganga | pt_PT |
| dc.subject | Solvent based lacquer | pt_PT |
| dc.subject | Water-based lacquer | pt_PT |
| dc.subject | Rotogravure | pt_PT |
| dc.subject | Staining | pt_PT |
| dc.subject | Denim | pt_PT |
| dc.title | Desenvolvimento de um filme de PVC/pu resistente ao manchamento pela ganga | pt_PT |
| dc.type | master thesis | |
| dspace.entity.type | Publication | |
| rcaap.rights | openAccess | pt_PT |
| rcaap.type | masterThesis | pt_PT |
| thesis.degree.name | Mestrado em Engenharia Química | pt_PT |