Publication
Desenvolvimento de um artigo de Silicone para Contract
| dc.contributor.advisor | Guedes, Anabela Maria Fonseca de Moura | |
| dc.contributor.author | Sousa, Rute Isabel Pereira de | |
| dc.date.accessioned | 2020-01-06T11:31:35Z | |
| dc.date.available | 2020-10-30T01:30:26Z | |
| dc.date.issued | 2019 | |
| dc.description.abstract | O presente trabalho foi realizado na empresa Monteiro Ribas S.A Revestimentos, e teve como principal objetivo o desenvolvimento de um revestimento de silicone para estofos contract. Inicialmente, foram realizados ensaios laboratoriais com diferentes formulações de resinas de silicone e respetivos catalisadores. Estudaram-se vários fatores tais como: temperatura de catalisação, massa de silicone e tipo de papel de gravação. Posteriormente foram realizados ensaios à escala piloto, nas melhores condições operatórias encontradas nos ensaios laboratoriais. Verificou-se que a temperatura ótima de catalisação do silicone é de 180ºC, e o papel de gravação utilizado tem bastante impacto no desenvolvimento do artigo. O silicone possui bastante aderência ao papel de gravação, não sendo possível a descolagem do mesmo. Também foi possível verificar que em todas as formulações testadas, após a mistura das matérias-primas, havia a formação de bolhas de ar, permitindo concluir que, numa escala industrial será necessário proceder à extração de ar, antes da sua utilização. De todos os papéis estudados, o papel F, foi o que permitiu um melhor release com todas as resinas testadas e, após diversos ensaios laboratoriais, verificou-se que a formulação que permitia a obtenção de melhores resultados foi a mistura de 50% resina RA, 50% resina RB, e 4,25% catalisador C. Este trabalho permitiu concluir que a substituição da camada top de PVC/PU por uma camada de silicone não é fácil. O papel de gravação tem de possuir uma superfície não siliconada, de modo a não aderir à camada de silicone. Neste trabalho, não foi possível o desenvolvimento de um artigo de silicone, com camadas semelhantes a um artigo convencional de poliuretano (PU) ou de policloreto de vinilo (PVC), devido à falta de aderência entre eles. Para ultrapassar este problema, seria necessário a aplicação de um primário antes da aplicação da camada de espuma. No entanto, esta solução implicaria custos adicionais para a empresa, na aquisição de equipamentos. O artigo de silicone produzido, quanto à sua caracterização física e química cumpre os requisitos de um artigo para contract com exceção na abrasão. | pt_PT |
| dc.description.abstract | This work was carried out at Monteiro Ribas S.A- Revestimentos, and its main objective was the developmente of a silicone pholstery for contract. Initially, laboratory tests were performed with different formulations of silicone resins and their catalysts. Several factors such as catalyst temperature, silicon mass and type of recording paper were studied. Subsequently, pilot scale tests were performed under the best operative conditions found in the laboratory tests. The optimal catalyzing temperature of the silicone has been found to be 180ºC, and the recording paper used has a great impact on the development of the article. The silicone has a good adhesion to the recording paper, it is not possible to take off. It was also possible to verify that in all formulations tested, after mixing the raw materials, air bubbles were formed, allowing to conclude that, on an industrial scale, air extraction will be necessary before its use. Of all the papers studied, F paper, from all of them, was the one that allowed a better release with all tested resins and, after several laboratory tests, it was verified that the formulation that allowed to obtain better results was the mixture of 50% RA resin, 50% RB resin, and 4.25% C catalyst. This work concluded that replacing the top layer of pvc / pu with a silicone layer is not easy. The embossing paper must have a non-silicon surface so as not to adhere to the silicone layer. In this work, it was not possible to develop a silicone article, with layers similar to a conventional polyurethane (PU) or polyvinyl chloride (PVC) article, due to the lack of adhesion between them. To overcome this problem, it would be necessary to apply a primer before applying the foam layer. However, this solution would entail additional costs for the company to purchase equipment. The silicone article produced, in terms of its physical and chemical characterization, meets the requirements of a contract article with the exception of abrasion. | pt_PT |
| dc.identifier.tid | 202296377 | pt_PT |
| dc.identifier.uri | http://hdl.handle.net/10400.22/15214 | |
| dc.language.iso | por | pt_PT |
| dc.subject | Silicone | pt_PT |
| dc.subject | Resinas de silicone | pt_PT |
| dc.subject | Policloreto de vinilo | pt_PT |
| dc.subject | Poliuretano, adesão | pt_PT |
| dc.subject | Silicone resins | pt_PT |
| dc.subject | Polyvinyl chloride | pt_PT |
| dc.subject | Polyurethane | pt_PT |
| dc.subject | Adhesion | pt_PT |
| dc.title | Desenvolvimento de um artigo de Silicone para Contract | pt_PT |
| dc.type | master thesis | |
| dspace.entity.type | Publication | |
| rcaap.rights | openAccess | pt_PT |
| rcaap.type | masterThesis | pt_PT |
| thesis.degree.name | Mestrado em Engenharia Química - Qualidade | pt_PT |