Preparação de materiais de carbono para a adsorção de compostos orgânicos voláteis (COV).
| dc.contributor.advisor | Freitas, Maria Madalena Alves de | |
| dc.contributor.advisor | Silva, Paula Cristina | |
| dc.contributor.advisor | Ribeiro, António Alfredo Crispim | |
| dc.contributor.author | Campos, Marisa Cristiana Soares da Costa | |
| dc.date.accessioned | 2013-11-06T15:41:36Z | |
| dc.date.available | 2013-11-06T15:41:36Z | |
| dc.date.issued | 2012 | |
| dc.description.abstract | A presente dissertação estudou a produção de carvão ativado a partir de resíduo de wet-blue, proveniente da indústria de curtumes, para a adsorção de compostos orgânicos voláteis, nomeadamente o acetato de etilo. Este estudo teve como principais objetivos: a otimização das condições de preparação de carvões ativados a partir deste tipo de resíduo; a avaliação do seu desempenho na adsorção do acetato de etilo e a correlação das propriedades texturais dos adsorventes com o seu desempenho na adsorção do COV. O método de ativação para a preparação dos carvões ativados foi a ativação química com hidróxido de potássio. Nesta etapa foi estudado o efeito da temperatura de ativação e da razão de impregnação KOH:precursor nas propriedades texturais. Nestes ensaios observou-se uma diminuição do rendimento de carbonizado com o aumento da temperatura de ativação e da razão KOH:precursor. Para a caracterização dos carvões ativados foram determinados os seus parâmetros texturais a partir das isotérmicas de adsorção/dessorção de N2 a 77 K. O carvão ativado com melhores propriedades texturais foi o ativado a 900ºC e com razão de impregnação de 3:1, m ca_900 3:1, com área superficial específica de 1902 m2/g, seguindo-se o carvão preparado a 800 ºC e com a mesma razão de impregnação, m ca_800 3:1, com área superficial específica de 1830 m2/g. Por fim, foi avaliado o desempenho do carvão ativado selecionado, m ca_800 3:1, na remoção de acetato de etilo de uma corrente gasosa. Foram efetuados ensaios de adsorção/ dessorção de acetato de etilo e o modelo de Langmuir foi ajustado aos resultados experimentais obtidos, tendo-se determinado uma capacidade de saturação de 500 mgCOV/ gadsorvente. | por |
| dc.description.abstract | This dissertation has studied the production of activated carbon from wet blue residue derived from the leather industry, for the adsorption of volatile organic compounds, such as ethyl acetate. This study had two main objectives: to optimize the preparation conditions of activated carbons from this type of waste, the assessment of their performance in the adsorption of ethyl acetate and the correlation of the textural properties of the adsorbents with their performance in the adsorption of VOCs. The activation method used for the preparation of activated carbons was chemical activation with potassium hydroxide. At this stage, the effect of activation temperature and KOH: precursor impregnation ratio in textural properties was studied. These tests showed a decrease in carbonization yield with the increase in the activation temperature and the KOH: precursor ratio. The textural characterization of activated carbons was performed by N2 adsorption / desorption of at 77 K. The activated carbon with better textural properties was the material activated at 900°C with an impregnation ratio KOH: precursor of 3:1, m ca_900 3:1, presenting a specific surface area of 1902 m2 / g. The activated carbon prepared at 800 º C and with the same impregnation ratio, m ca_800 3:1, presented a specific surface area of 1830 m2 / g. Finally, the performance of the selected activated carbon, m ca_800 3:1, for the removal of ethyl acetate from a gaseous stream was evaluated. Tests were performed for adsorption / desorption of ethyl acetate. Langmuir model was adjusted to the experimental results and a saturation capacity of 500 mgVOC / gadsorbent was obtained. | por |
| dc.identifier.uri | http://hdl.handle.net/10400.22/2570 | |
| dc.language.iso | por | por |
| dc.peerreviewed | yes | por |
| dc.publisher | Instituto Politécnico do Porto. Instituto Superior de Engenharia do Porto | por |
| dc.subject | COV | por |
| dc.subject | Carvão ativado | por |
| dc.subject | Wet-blue | por |
| dc.subject | Ativação química | por |
| dc.subject | isotérmico de adsorção | por |
| dc.subject | Acetato de etilo | por |
| dc.subject | VOC | por |
| dc.subject | Activated carbon | por |
| dc.subject | Wet-blue | por |
| dc.subject | Chemical activation | por |
| dc.subject | Adsorption isotherms | por |
| dc.subject | Ethyl acetate | por |
| dc.title | Preparação de materiais de carbono para a adsorção de compostos orgânicos voláteis (COV). | por |