Redução de variações nas propriedades viscoelásticas de compostos de borracha
| dc.contributor.advisor | Pimenta, Maria Paula Moreira de Carvalho Amorim Neto | |
| dc.contributor.author | Grande, Inês Alonso da Silva Campo | |
| dc.date.accessioned | 2020-11-03T12:34:02Z | |
| dc.date.available | 2023-10-22T00:31:24Z | |
| dc.date.issued | 2020 | |
| dc.description.abstract | A presente dissertação descreve o trabalho desenvolvido na Continental em parceria com o ISEP no âmbito da unidade curricular Dissertação/Estágio do curso de Mestrado em Engenharia Química. A dissertação apresentada teve como objetivo principal a identificação, no processo de mistura, de potenciais fontes de variações nas propriedades viscoelásticas de compostos de borracha e a implementação de soluções que as permitam reduzir. Para o efeito estudou-se a influência de variáveis afetas a algumas matérias primas e ao processo. Relativamente às matérias primas estudou-se a tolerância de pesagem de enxofre e as propriedades viscoelásticas de resinas e borrachas; relativamente às variáveis afetas ao processo foram estudadas o tempo e temperatura do plateau de silanização e número de rpm e revoluções no dry e wet mixing. Para cada uma das variáveis em estudo realizaram-se diferentes ensaios de acordo com o plano de experiências disponível. De seguida relacionaram-se as propriedades dos diferentes ensaios e avaliou-se individualmente a sua variação no intervalo de aceitação, que é considerado impactante quando é superior a 5%. No estudo da influência de pesagem de enxofre usou-se um composto de tela têxtil e as propriedades onde se registou maior impacto foram as físicas e reométricas. Para avaliar a influência das propriedades viscoelásticas das resinas produziu-se o composto de piso de base e o composto de piso de sílica I dado que apresenta resinas de diferentes origens na sua produção, neste caso as propriedades mais impactantes foram as físicas, RPA e a adesividade. Para as propriedades viscoelásticas da borracha avaliou-se o comportamento do composto de camada estanque e o composto de piso de sílica II. Neste caso o impacto foi sentido em propriedades de todos os grupos: físicas, reológicas e RPA. Relativamente ao processo foram analisadas as condições da reação de silanização e para isso usou-se o composto de piso de inverno onde todas as propriedades se mostraram impactantes. Por fim estudou-se o número de rpm e revoluções no dry e wet mixing. Para este estudo avaliouse o comportamento do composto de parede para o qual na etapa de dry mixing todas as propriedades, à exceção da densidade, apresentaram um impacto considerável com ênfase nas propriedades físicas e de RPA. Na etapa de wet mixing as propriedades mais impactantes foram as físicas e de RPA. | pt_PT |
| dc.description.abstract | The present dissertation describes the work developed in Continental, in partnership with ISEP, for the discipline of Dissertação/Estágio encapsuled in its Master’s Degree in Chemical Engineering. It has as its main goal the identification, during the mixing process, of potential sources of variations of the viscoelastic properties of rubber compounds, and the implementation of solutions that can reduce them. For this goal, the influence of variables regarding the raw materials used and the process itself were studied. Regarding the raw materials, the sulfur weight tolerance and the viscoelastic properties of rubbers were studied, while for the process variables the focus was on the time, plateau silanization temperature and the number of r.p.m. and revolutions in the dry and wet mixing. For each studied variable, several different trials were conducted according to the available experiences plan. Afterwards, relationships between the properties of the different trials were created and its variations in the acceptance interval evaluated, as it is considered impactful when is over 5%. While studying the sulfur weight tolerance a compound made of textile screen was used and the most impactful properties were the physic and rheometric ones. In order to evaluate the influence of the viscoelastic properties of the resins a base tread compound was produced, along with a silica I tread compound, as they have different resins in its composition, and in this case the most impactful properties were the physic, RPA and cohesiveness. For the study of the viscoelastic properties of the rubbers, the behaviors of the watertight layer composite and the silica II base tread were evaluated, with the findings being the opposite in each category: physic, rheologic and RPA. As for the process itself the silanization rection conditions were analyzed, using the winter base tread, where all properties were deemed impactful. Lastly, the number of r.p.m. and revolutions in the dry and wet mixing processes were studied. For this study the behavior of the wall compound was evaluated. During the dry mixing stage, all of its properties except for its density showed a considerable impact, more so in its physic and RPA properties. As for the wet mixing stage, the most impactful properties were the physic and RPA ones. | pt_PT |
| dc.identifier.tid | 202533328 | pt_PT |
| dc.identifier.uri | http://hdl.handle.net/10400.22/16409 | |
| dc.language.iso | por | pt_PT |
| dc.subject | Indústria de pneus | pt_PT |
| dc.subject | Propriedades viscoelásticas | pt_PT |
| dc.subject | Processo de mistura | pt_PT |
| dc.subject | Reação silanização | pt_PT |
| dc.subject | Tire industry | pt_PT |
| dc.subject | Viscoelastic properties | pt_PT |
| dc.subject | Mixing process | pt_PT |
| dc.subject | Silanization reaction | pt_PT |
| dc.title | Redução de variações nas propriedades viscoelásticas de compostos de borracha | pt_PT |
| dc.type | master thesis | |
| dspace.entity.type | Publication | |
| rcaap.rights | openAccess | pt_PT |
| rcaap.type | masterThesis | pt_PT |
| thesis.degree.name | Mestrado em Engenharia Química - Energia e Biorrefinaria | pt_PT |
Files
Original bundle
1 - 1 of 1
No Thumbnail Available
- Name:
- DM_InesGrande_2020_MEQ.pdf
- Size:
- 6.57 MB
- Format:
- Adobe Portable Document Format