Loading...
2 results
Search Results
Now showing 1 - 2 of 2
- Expanding the applications of the wear-resistant titanium aluminum nitride thin-film to include temperature sensingPublication . Martins, Bruno; Patacas, Carlos; Cavaleiro, Albano; Faia, Pedro; Zorro, Fátima; Carbo-Argibay, Enrique; FGerreira, Paulo J.; Fernandes, Filipe; Fernandes, FilipeThis study investigates an approach to temperature sensing by integrating Titanium Aluminum Nitride (TiAlN), originally engineered for wear and corrosion applications, as a temperature sensor within a multilayered thin film system. A nitride multilayer system was developed by physical vapor deposition (PVD) using a single four-target magnetron sputtering chamber; intermediate vacuum interruption steps were employed for masking procedures. The multilayer architecture design aimed to provide the sensor layer with mechanical protection and electrical shielding. Structural and electrical characterization of the TiAlN single layer revealed semiconductor behavior and stable electrical resistance up to 750 °C, with minimal signal stabilization requirements. Despite the higher Al content, the TiAlN temperature sensor exhibited a cubic crystal structure characterized by diffuse nanolayers, resulting from a two-fold rotational deposition and target configuration. A detailed examination of the multilayer system cross-section containing the TiAlN sensor was conducted using scanning transmission electron microscopy (STEM). The analysis revealed its columnar morphology with the presence of typical PVD growth defects, including voids and droplets. While the presence of these defects may impact the electrical characteristics of the sensor, the selected experimental conditions effectively maintained the structural integrity of the multilayer system despite the vacuum interruptions caused by masking procedures. Validation experiments confirmed the functionality of the multilayer system for temperature measurements up to 400 °C. The signal acquisition system addressed room temperature resistance variations and low sensitivity (thermistor coefficient ∼100 K), resulting in a measured error of approximately 6%. This study demonstrates promising results of TiAlN as a temperature sensor within a multilayered system, expanding its range of potential applications.
- Tribological Comparison of Coatings Produced by PVD Sputtering for Application on Combustion Piston RingsPublication . Ferreira, Ney Francisco; Neis, Patric Daniel; Fernandes, Filipe; Poletto, Jean Carlos; Yaqub, Talha Bin; Cavaleiro, Albano; Vilhena, Luís; Ramalho, AmílcarThis article compares the tribological performance of coatings produced by PVD sputtering. Transition metal dichalcogenide (TMD) coatings doped with carbon (WSC and MoSeC) and nitrogen (WSN and MoSeN) and a conventional diamond-like carbon (DLC) coating are compared. The tribological evaluation was oriented towards the use of coatings on piston rings. Block-on-ring tests in a condition lubricated with an additive-free polyalphaolefin (PAO 8) and at temperatures of 30, 60, and 100 °C were carried out to evaluate the coatings in boundary lubrication conditions. A load scanner test was used to evaluate dry friction and scuffing propensity. In addition to WSN, all other TMD coatings (WSC, MoSeC, and MoSeN) exhibited lower friction than DLC in dry and lubricated conditions. The study reveals that WSC, among TMD coatings, offers promising results, with significantly lower friction levels than DLC, while demonstrating reduced wear and a lower risk of metal adhesion. These findings suggest that WSC may be a viable alternative to DLC in piston rings, with potential benefits for reducing fuel consumption and increasing engine durability.