Browsing by Author "Ribeiro, G. M."
Now showing 1 - 4 of 4
Results Per Page
Sort Options
- Effects of sulphurization time on Cu2ZnSnS4 absorbers and thin films solar cells obtained from metallic precursorsPublication . Fernandes, P. A.; Salomé, P. M. P.; Sartori, A. F.; Malaquias, J.; Cunha, A. F. da; Schubert, Björn-Arvid; González, J. C.; Ribeiro, G. M.We report the results of a study of the sulphurization time effects on Cu2ZnSnS4 absorbers and thin film solar cells prepared from dc-sputtered tackedmetallic precursors. Three different time intervals, 10 min, 30min and 60 min, at maximum sulphurization temperature were considered. The effects of this parameter' change were studied both on the absorber layer properties and on the final solar cell performance. The composition, structure, morphology and thicknesses of the CZTS layers were analyzed. The electrical characterization of the absorber layer was carried out by measuring the transversal electrical resistance of the samples as a function of temperature. This study shows an increase of the conductivity activation energy from 10 meV to 54meV for increasing sulphurization time from 10min to 60min. The solar cells were built with the following structure: SLG/Mo/CZTS/CdS/i-ZnO/ZnO:Al/Ni:Al grid. Several ac response equivalent circuit models were tested to fit impedance measurements. The best results were used to extract the device series and shunt resistances and capacitances. Absorber layer's electronic properties were also determined using the Mott–Schottky method. The results show a decrease of the average acceptor doping density and built-in voltage, from 2.0 1017 cm−3 to 6.5 1015 cm−3 and from 0.71 V to 0.51 V, respectively, with increasing sulphurization time. These results also show an increase of the depletion region width from approximately 90 nm–250 nm.
- Electronic Conduction Mechanisms and Defects in Polycrystalline Antimony SelenidePublication . Cifuentes, N.; Ghosh, Santunu; Shongolova, A.; Correia, M. R.; Salomé, P. M. P.; Fernandes, P. A.; Ranjbar, S.; Garud, S.; Vermang, B.; Ribeiro, G. M.; González, J. C.A study of the electronic conduction mechanisms and electrically active defects in polycrystalline Sb2Se3 is presented. It is shown that for temperatures above 200 K, the electrical transport is dominated by thermal emission of free holes, ionized from shallow acceptors, over the intergrain potential barriers. In this temperature range, the temperature dependence of the mobility of holes, limited by the intergrain potential barriers, is the main contributor to the observed thermal activation energy of the conductivity of 485 meV. However, at lower temperatures, nearest-neighbor and Mott variable range hopping transport in the bulk of the grains turn into the dominant conduction mechanisms. Important parameters of the electronic structure of the Sb2Se3 thin film such as the average intergrain potential barrier height ϕ = 391 meV, the intergrain trap density Nt = 3.4 × 1011 cm−2, the shallow acceptor ionization energy EA0 = 124 meV, the acceptor density NA = 1 × 1017 cm−3, the net donor density ND = 8.3 × 1016 cm−3, and the compensation ratio k = 0, 79 were determined from the analysis of these measurements.
- Hopping conduction and persistent photoconductivity in Cu2ZnSnS4 thin filmsPublication . González, J. C.; Ribeiro, G. M.; Viana, E. R.; Fernandes, P. A.; Salomé, P. M. P.; Gutíerrez, K.; Abelenda, A.; Matinaga, F. M.; Leitão, J. P.; Cunha, A. F. daThe temperature dependence of electrical conductivity and the photoconductivity of polycrystalline Cu2ZnSnS4 were investigated. It was found that at high temperatures the electrical conductivity was dominated by band conduction and nearest-neighbour hopping. However, at lower temperatures, both Mott variable-range hopping (VRH) and Efros–Shklovskii VRH were observed. The analysis of electrical transport showed high doping levels and a large compensation ratio, demonstrating large degree of disorder in Cu2ZnSnS4. Photoconductivity studies showed the presence of a persistent photoconductivity effect with decay time increasing with temperature, due to the presence of random local potential fluctuations in the Cu2ZnSnS4 thin film. These random local potential fluctuations cannot be attributed to grain boundaries but to the large disorder in Cu2ZnSnS4.
- Photoluminescence and electrical study of fluctuating potentials in Cu2ZnSnS4-based thin filmsPublication . Leitão, J. P.; Santos, Nuno Miguel; Fernandes, P. A.; Salomé, P. M. P.; Cunha, A. F. da; González, J. C.; Ribeiro, G. M.; Matinaga, F. M.In this work, we investigated structural, morphological, electrical, and optical properties from a set of Cu2ZnSnS4 thin films grown by sulfurization of metallic precursors deposited on soda lime glass substrates coated with or without molybdenum. X-ray diffraction and Raman spectroscopy measurements revealed the formation of single-phase Cu2ZnSnS4 thin films. A good crystallinity and grain compactness of the film was found by scanning electron microscopy. The grown films are poor in copper and rich in zinc, which is a composition close to that of the Cu2ZnSnS4 solar cells with best reported efficiency. Electrical conductivity and Hall effect measurements showed a high doping level and a strong compensation. The temperature dependence of the free hole concentration showed that the films are nondegenerate. Photoluminescence spectroscopy showed an asymmetric broadband emission. The experimental behavior with increasing excitation power or temperature cannot be explained by donor-acceptor pair transitions. A model of radiative recombination of an electron with a hole bound to an acceptor level, broadened by potential fluctuations of the valence-band edge, was proposed. An ionization energy for the acceptor level in the range 29–40 meV was estimated, and a value of 172 ±2 meV was obtained for the potential fluctuation in the valence-band edge.