Título: Influence of the abrasive particles size in the micro-abrasion wear tests of TiAlSiN thin coatings
Autor: Andrade, M. F. C.
Martinho, R. P.
Silva, Francisco J. G.
Alexandre, R. J. D.
Baptista, A. P. M.
Palavras-chave: Abrasive particles
Hard coatings
Data: 2009
Editora: Elsevier
Relatório da Série N.º: Wear; Vol. 267, Issues 1-4
Resumo: Ball rotating micro-abrasion tribometers are commonly used to carry out wear tests on thin hard coatings. In these tests, different kinds of abrasives were used, as alumina (Al2O3), silicon carbide (SiC) or diamond. In each kind of abrasive, several particle sizes can be used. Some studies were developed in order to evaluate the influence of the abrasive particle shape in the micro-abrasion process. Nevertheless, the particle size was not well correlated with the material removed amount and wear mechanisms. In this work, slurry of SiC abrasive in distilled water was used, with three different particles size. Initial surface topography was accessed by atomic force microscopy (AFM). Coating hardness measurements were performed with a micro-hardness tester. In order to evaluate the wear behaviour, a TiAlSiN thin hard film was used. The micro-abrasion tests were carried out with some different durations. The abrasive effect of the SiC particles was observed by scanning electron microscopy (SEM) both in the films (hard material) as in the substrate (soft material), after coating perforation. Wear grooves and removed material rate were compared and discussed.
Peer review: yes
URI: http://hdl.handle.net/10400.22/4517
ISSN: 0043-1648
Versão do Editor: http://www.sciencedirect.com/science/article/pii/S004316480900235X
Aparece nas colecções:ISEP – CIDEM – Artigos

Ficheiros deste registo:
Ficheiro Descrição TamanhoFormato 
ART_MAndrade_2009_CIDEM.pdf1,48 MBAdobe PDFVer/Abrir

FacebookTwitterDeliciousLinkedInDiggGoogle BookmarksMySpace
Formato BibTex MendeleyEndnote Degois 

Todos os registos no repositório estão protegidos por leis de copyright, com todos os direitos reservados.