Utilize este identificador para referenciar este registo: http://hdl.handle.net/10400.22/4175
Título: Cutting forces and wear analysis of Si3N4 diamond coated tools in high speed machining
Autor: Martinho, R. P.
Silva, Francisco J. G.
Baptista, A. P. M.
Palavras-chave: HSM
Turning
Coatings
Diamond
Tool wear
Data: 2008
Editora: Elsevier
Relatório da Série N.º: Vacuum; Vol. 82, Issue 12
Resumo: Si3N4 tools were coated with a thin diamond film using a Hot-Filament Chemical Vapour Deposition (HFCVD) reactor, in order to machining a grey cast iron. Wear behaviour of these tools in high speed machining was the main subject of this work. Turning tests were performed with a combination of cutting speeds of 500, 700 and 900 m min−1, and feed rates of 0.1, 0.25 and 0.4 mm rot−1, remaining constant the depth of cut of 1 mm. In order to evaluate the tool behaviour during the turning tests, cutting forces were analyzed being verified a significant increase with feed rate. Diamond film removal occurred for the most severe set of cutting parameters. It was also observed the adhesion of iron and manganese from the workpiece to the tool. Tests were performed on a CNC lathe provided with a 3-axis dynamometer. Results were collected and registered by homemade software. Tool wear analysis was achieved by a Scanning Electron Microscope (SEM) provided with an X-ray Energy Dispersive Spectroscopy (EDS) system. Surface analysis was performed by a profilometer.
Peer review: yes
URI: http://hdl.handle.net/10400.22/4175
ISSN: 0042-207X
Versão do Editor: http://www.sciencedirect.com/science/article/pii/S0042207X08001334
Aparece nas colecções:ISEP – CIDEM – Artigos

Ficheiros deste registo:
Ficheiro Descrição TamanhoFormato 
ART_RMartinho_2008_CIDEM.pdf1,18 MBAdobe PDFVer/Abrir


FacebookTwitterDeliciousLinkedInDiggGoogle BookmarksMySpace
Formato BibTex MendeleyEndnote Degois 

Todos os registos no repositório estão protegidos por leis de copyright, com todos os direitos reservados.