Título: Study of vanadium doped ZnO films prepared by dc reactive magnetron sputtering at different substrate temperatures
Autor: Meng, Lijian
Teixeira, Vasco
Santos, M. P.
Palavras-chave: Zinc Oxide
Vanadium Oxide
Thin Films
Sputtering
Optical Properties
Data: 2013
Editora: American Scientific Publishers
Relatório da Série N.º: Journal of Nanoscience and Nanotechnology; Vol. 13, Issue 2
Resumo: ZnO films doped with vanadium (ZnO:V) have been prepared by dc reactive magnetron sputtering technique at different substrate temperatures (RT–500 C). The effects of the substrate temperature on ZnO:V films properties have been studied. XRD measurements show that only ZnO polycrystalline structure has been obtained, no V2O5 or VO2 crystal phase can be observed. It has been found that the film prepared at low substrate temperature has a preferred orientation along the (002) direction. As the substrate temperature is increased, the (002) peak intensity decreases. When the substrate temperature reaches the 500 C, the film shows a random orientation. SEM measurements show a clear formation of the nano-grains in the sample surface when the substrate temperature is higher than 400 C. The optical properties of the films have been studied by measuring the specular transmittance. The refractive index has been calculated by fitting the transmittance spectra using OJL model combined with harmonic oscillator.
Peer review: yes
URI: http://hdl.handle.net/10400.22/3227
ISSN: 1533-4880
Versão do Editor: http://www.ingentaconnect.com/content/asp/jnn/2013/00000013/00000002/art00138?token=004611e1d5a666f3a7b6c2a4038425e6b66477e3f2a49264f655d375c6b68763050210
Aparece nas colecções:ISEP – DFI – Artigos

Ficheiros deste registo:
Ficheiro Descrição TamanhoFormato 
ART_LijianMeng_2013DFI.pdf1,61 MBAdobe PDFVer/Abrir    Acesso Restrito. Solicitar cópia ao autor!


FacebookTwitterDeliciousLinkedInDiggGoogle BookmarksMySpace
Formato BibTex MendeleyEndnote Degois 

Todos os registos no repositório estão protegidos por leis de copyright, com todos os direitos reservados.