Título: Structural modification of TiO2 nanorod films with an influence on the photovoltaic efficiency of a dye-sensitized solar cell (DSSC).
Autor: Meng, Lijian
Li, Can
Santos, M. P.
Palavras-chave: TiO2
Nanorod
Sputtering
DSSC
Data: 2013
Editora: Springer
Relatório da Série N.º: Journal of Inorganic and Organometallic Polymers and Materials; Vol. 23, Issue 4
Resumo: TiO2 nanorod films have been deposited on ITO substrates by dc reactive magnetron sputtering technique. The structures of these nanorod films were modified by the variation of the oxygen pressure during the sputtering process. Although all these TiO2 nanorod films deposited at different oxygen pressures show an anatase structure, the orientation of the nanorod films varies with the oxygen pressure. Only a very weak (101) diffraction peak can be observed for the TiO2 nanorod film prepared at low oxygen pressure. However, as the oxygen pressure is increased, the (220) diffraction peak appears and the intensity of this diffraction peak is increased with the oxygen pressure. The results of the SEM show that these TiO2 nanorods are perpendicular to the ITO substrate. At low oxygen pressure, these sputtered TiO2 nanorods stick together and have a dense structure. As the oxygen pressure is increased, these sputtered TiO2 nanorods get separated gradually and have a porous structure. The optical transmittance of these TiO2 nanorod films has been measured and then fitted by OJL model. The porosities of the TiO2 nanorod films have been calculated. The TiO2 nanorod film prepared at high oxygen pressure shows a high porosity. The dye-sensitized solar cells (DSSCs) have been assembled using these TiO2 nanorod films prepared at different oxygen pressures as photoelectrode. The optimum performance was achieved for the DSSC using the TiO2 nanorod film with the highest (220) diffraction peak and the highest porosity.
Peer review: yes
URI: http://hdl.handle.net/10400.22/3226
ISSN: 1574-1443
1574-1451
Versão do Editor: http://link.springer.com/article/10.1007%2Fs10904-013-9842-9
Aparece nas colecções:ISEP – DFI – Artigos

Ficheiros deste registo:
Ficheiro Descrição TamanhoFormato 
ART_LijianMeng_2013_DFI.pdf695,23 kBAdobe PDFVer/Abrir


FacebookTwitterDeliciousLinkedInDiggGoogle BookmarksMySpace
Formato BibTex MendeleyEndnote Degois 

Todos os registos no repositório estão protegidos por leis de copyright, com todos os direitos reservados.